Nanoscale Investigation of Platinum Nanoparticles on SrTiO3 Grown via Physical Vapor Deposition and Atomic Layer Deposition

Steven Christensen

doi:https://doi.org/10.21985/N2N449

Work

Nanoscale Investigation of Platinum Nanoparticles on SrTiO3 Grown via Physical Vapor Deposition and Atomic Layer Deposition

Public Deposited

Download PDF

Download All Files (.zip)

This dissertation examines growth of platinum nanoparticles from vapor deposition on SrTiO3 using a characterization approach that combines imaging techniques and X-ray methods. The primary suite of characterization probes includes atomic force microscopy (AFM), grazing-incidence small-angle X-ray scattering (GISAXS), X-ray fluorescence (XRF), scanning electron microscopy (SEM), and X-ray absorption spectroscopy (XAS). The vapor deposition techniques include physical vapor deposition (PVD) by evaporation and atomic layer deposition (ALD). For the PVD platinum study, AFM/XRF showed ~10 nm nanoparticles separated by an average of 100 nm. The combination of AFM, GISAXS, and XRF indicated that the nanoparticles observed with AFM were actually comprised of closely spaced, smaller nanoparticles. These conclusions were supported by high-resolution SEM. The unusual behavior of platinum nanoparticles to aggregate without coalescence or sintering was observed previously by other researchers using transmissision electron microscopy (TEM). Platinum nanoparticle growth was also investigated on SrTiO3 (001) single crystals using ALD to nucleate nanoparticles that subsequently grew and coalesced into granular films as the ALD progresses. The expected growth rate for the early stages of ALD showed a two-fold increase which was attributed to the platinum deposition occurring faster on the bare substrate. Once the nanoparticles had coalesced into a film, steady state ALD growth proceeded. The formation of nanoparticles was attributed to the atomic diffusion of platinum atoms on the surface in addition to direct growth from the ALD precursor gases. The platinum ALD nanoparticles were also studied on SrTiO3 nanocube powders. The SrTiO3 nanocubes average 60 nm on a side and the cube faces have a {001} orientation. The ALD proceeded in a similar fashion as on the single crystal substrates where the deposition rate was twice as fast as the steady state growth rate. The Pt nanoparticle size increased linearly starting at ~0.7 nm for 1 ALD cycle to ~3 nm for 5 ALD cycles. The platinum chemical state was also investigated using X-ray absorption spectroscopy. Platinum nanoparticles ~1 nm or smaller tended to be oxidized. For larger nanoparticles, the platinum state systematically approached that of bulk platinum metal as the size (number of ALD cycles) increased. The platinum loading was exceptionally low, ~ 0.001 mg per square centimeter.

Last modified