This study investigated the precipitation
strengthening of the binary Al-0.14wt% Sc,
0.16% Ti alloy system. Ingots of Al-2.1wt% Sc
and Al-4.68wt% Ti were melted together, and
the nucleation, growth, and coarsening of
precipitates were analyzed. The microstructural
evolution of the nanoscale L12 precipitates
phase was examined with Vickers
microhardness testing,...